Makine Mühendisliği Bölümü Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.11779/1944
Browse
2 results
Search Results
Article Nbmovta Refractory High-Entropy Alloy Incorporated Wni Matrix Composite as a Future Plasma-Facing Material: Evaluation of Mechanical Properties and Helium Ion Irradiation Behavior(Elsevier Sci Ltd, 2025) Öveçoğlu, M. Lutfi; Filiz, Kaan; Karaguney, Zahide; Gokaydin, Eyupcan; Bozkurt, Yasin; Ozbasmaci, Ceren; Ovecoglu, M. Lutfi; 01. MEF University; 02.03. Department of Mechanical Engineering; 02. Faculty of EngineeringRefractory high-entropy alloys (RHEAs) have gained attention in the last decades with their high mechanical strength, self-healing mechanism, and high irradiation resistance. These materials are evaluated to have a high potential as plasma-facing materials for fusion reactors. In this study, helium ion irradiation and mechanical behaviors of the RHEA-reinforced WNi matrix composites were investigated based on this perspective. Equimolar molybdenum, niobium, tantalum and vanadium powders were mechanically alloyed for 6 h to produce NbMoVTa RHEA with a single BCC phase. Then, different amounts (10, 20, 30, and 40 wt%) of RHEA were added into the W1Ni (containing 99 wt% W and 1 wt% Ni) matrix by planetary ball milling for 72 h. Consolidation was conducted by spark plasma sintering technique (1410 degrees C, 1 min). X-ray diffraction, scanning electron microscopy coupled with energy dispersion spectroscopy, and Archimedes' density analyses were performed on the composites. Moreover, wear and hardness properties of the composites were examined, and the lowest specific wear rate (0.59 mm3/N.m x 10- 5) and the highest hardness value (10.10 GPa) were found for the W1Ni-40RHEA composite. Helium irradiation was exposed to the composites to observe their irradiation resistance. It was observed that the lowest increment and the least deformation were obtained with the SPS'ed W1Ni-40RHEA composite. With the analysis of He+ irradiation, it was determined that the effect of radiation on mechanical properties is irrelevant. Also, it was observed that the addition of RHEA into the W matrix can create a high potential for using plasma-facing material. Moreover, it decreased the problems of tungsten against He+ irradiation.Article Citation - WoS: 1Mechanochemical Synthesis and Characterization of Nanostructured Erb4 and Ndb4 Rare-Earth Tetraborides(John Wiley and Sons Inc, 2024) Boztemur, B.; Öveçoğlu, M. Lutfi; Derin, B.; Öveçoğlu, M.L.; Li, J.; Ağaoğulları, D.; 02.03. Department of Mechanical Engineering; 02. Faculty of Engineering; 01. MEF UniversityRare-earth borides have become very popular in recent decades with high mechanical strength, melting point, good corrosion, wear, and magnetic behavior. However, the production of these borides is very challenging and unique. The production of ErB4 and NdB4 nanopowders via mechanochemical synthesis (MCS) is reported in this study first time in the literature. Er2O3 or Nd2O3, B2O3, and Mg initial powders are mechanically alloyed for different milling times to optimize the process. Rare-earth borides with MgO phases are synthesized, then MgO is removed with HCl acid. The nanostructured rare-earth tetraboride powders are analyzed using X-ray diffraction (XRD). Based on the XRD, ErB4 powders are produced successfully at the end of the 5 h milling. However, the NdB4 phase does not occur as the stoichiometric ratio, so the B2O3 amount is decreased to nearly 35 wt%. When the amount of B2O3 is decreased to 20 wt%, NdB4 and NdB6 phases are 50:50 according to the Rietveld analysis. However, a homogenous NdB4 phase is obtained with 30 wt% loss of B2O3. The average particle sizes of ErB4 and NdB4 powders are nearly 100.4 and 85.6 nm, respectively. The rare-earth tetraborides exhibit antiferromagnetic-to-paramagnetic-like phase transitions at 18 and 8.53 K, respectively. © 2024 The Author(s). Advanced Engineering Materials published by Wiley-VCH GmbH.